Yixing Hengyuan Ceramic Technology Co., Ltd.
Yixing Hengyuan Ceramic Technology Co., Ltd.
Add to Cart
| Attribute | Value |
|---|---|
| Material | Ceramic Tube |
| Color | Yellow Or White |
| Temperature Capability | High Heat Resistant |
| Dielectric constant | 10εr |
| OEM,ODM | Acceptable |
| Origin | WUXI JIANGSU CHINA |
| MOQ | 100 |
| Package | Carton |
Isostatic pressure forming technology is a key process in manufacturing wear-resistant alumina ceramic tubes. This advanced method forms pipeline materials under uniform pressure, ensuring structural uniformity and stability. Compared to traditional molding methods, this technology offers superior precision, lower scrap rates, and significantly improved product quality and production efficiency.
| Material | Unit | A95% Alumina Ceramics | A97% Alumina Ceramics | A99% Alumina Ceramics | A99.7% Alumina Ceramics |
|---|---|---|---|---|---|
| Density | g/cm³ | 3.6 | 3.72 | 3.85 | 3.85 |
| Flexural Strength | Mpa | 290 | 300 | 350 | 350 |
| Compressive Strength | Mpa | 3300 | 3400 | 3600 | 3600 |
| Modulus of Elasticity | Gpa | 340 | 350 | 380 | 380 |
| Impact Resistance | MPam1/2 | 3.9 | 4 | 5 | 5 |
| Weibull Modulus | M | 10 | 10 | 11 | 11 |
| Vickers Hardness | HV0.5 | 1800 | 1850 | 1900 | 1900 |
| Thermal Expansion Coefficient | 10-6K-1 | 5.0-8.3 | 5.0-8.3 | 5.4-8.3 | 5.4-8.3 |
| Thermal Conductivity | W/Mk | 23 | 24 | 27 | 27 |
| Thermal Shock Resistance | △T℃ | 250 | 250 | 270 | 270 |
| Maximum Use Temperature | ℃ | 1600 | 1600 | 1650 | 1650 |
| Volume Resistivity at 20℃ | Ω | ≥1014 | ≥1014 | ≥1014 | ≥1014 |
| Dielectric Strength | KV/mm | 20 | 20 | 25 | 25 |
| Dielectric constant | εr | 10 | 10 | 10 | 10 |