The specialized ceramic machine for crushing equipment operates by directing large pieces of glass vertically from the upper part into a high-speed rotating impeller. Under centrifugal force, the material collides at high speed with another portion distributed in an umbrella shape around the impeller. After impact, the material forms vortices between the impeller and casing, undergoing multiple collisions and friction cycles for thorough crushing. The processed material discharges from the lower part, completing a closed-loop cycle controlled by screening equipment to achieve the desired particle size.
| Attribute | Value |
|---|---|
| Material | Alumina Ceramic Crusher Parts |
| Color | Yellow Or White |
| Maximum Use Temperature | 1600-1650℃ |
| Wear Resistance | High Wear resistance |
| OEM,ODM | Acceptable |
| Origin | WUXI JIANGSU CHINA |
| MOQ | 100 |
| Package | Carton |
| Material | Unit | A95% Alumina Ceramics | A97% Alumina Ceramics | A99% Alumina Ceramics | A99.7% Alumina Ceramics |
|---|---|---|---|---|---|
| Density | g/cm³ | 3.6 | 3.72 | 3.85 | 3.85 |
| Flexural Strength | Mpa | 290 | 300 | 350 | 350 |
| Compressive Strength | Mpa | 3300 | 3400 | 3600 | 3600 |
| Modulus of Elasticity | Gpa | 340 | 350 | 380 | 380 |
| Impact Resistance | MPam1/2 | 3.9 | 4 | 5 | 5 |
| Weibull Modulus | M | 10 | 10 | 11 | 11 |
| Vickers Hardness | HV0.5 | 1800 | 1850 | 1900 | 1900 |
| Thermal Expansion Coefficient | 10-6K-1 | 5.0-8.3 | 5.0-8.3 | 5.4-8.3 | 5.4-8.3 |
| Thermal Conductivity | W/Mk | 23 | 24 | 27 | 27 |
| Thermal Shock Resistance | △T℃ | 250 | 250 | 270 | 270 |
| Maximum Use Temperature | ℃ | 1600 | 1600 | 1650 | 1650 |
| Volume Resistivity at 20℃ | Ω | ≥1014 | ≥1014 | ≥1014 | ≥1014 |
| Dielectric Strength | KV/mm | 20 | 20 | 25 | 25 |
| Dielectric constant | εr | 10 | 10 | 10 | 10 |